Flexible electronic devices

ABSTRACT

The present disclosure is related to display panels, especially to flexible electronic devices. By means of adding an inorganic membrane with surface roughness between a bonding layer and a PI film, in order to effectively improve the dimensional stability of plastic substrate and the water/oxygen barrier property of flexible substrate during the PI film fabrication and the follow-up process, improving the yield of good products and prolonging the working life thereof.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a continuation application of applicationSer. No. 14/152,732 filed on Jan. 10, 2014, and claims priority to andthe benefit of Chinese Patent Application No. CN 201310073718.9, filedon Mar. 8, 2013, the entire content of each of which is incorporatedherein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present disclosure relates to display devices, more specifically, toelectronic devices.

2. Description of the Related Art

A flexible display device can display information even though it isfolded or bent, by means of forming display thereof unit on a flexiblesubstrate. Therefore, the flexible display device is with a vastapplication prospect in field of portable electronic devices, wherein,the display equipments adopting the flexible display device comprise:Cholesteric Liquid Crystal Display (“LCD”, hereinafter), ElectrophoresisDevice and Organic Light-emitting Diode (“OLED”, hereinafter) and so on.

OLED mainly consists of a cathode layer where electrons can be injected,and an anode layer where holes can be injected. A voltage of suitablepolarity is applied between the cathode layer and the anode layer tocombine the holes and the electrons to release energy by lighting, i.e.,electrofluorescence. Thus, OLED is Self-Illumination, and consequently,the back-lighting is unnecessary. Therefore, a light, thin and flexibledisplay can be achieved by OLED. In the related art, the OLED iscombined with a flexible substrate and a TFT backplane to fabricate aflexible OLED device, where the flexible substrate technology andde-bonding technology is pivotal.

The flexible substrates applied in the flexible display devices mainlyinclude: organic plastic substrate, such as PC, PET, PEN, PES, PI,composite material substrate made from organic material and inorganicmaterial by means of laminating or other methods and metal substratecontaining stainless steel or aluminum.

Presently, the usage of the flexible substrate mainly includes thefollowing two methods, i.e., the pre-prepared sheet material isprovided, then it is bonded to a rigid substrate, such as glass, bybinder; and the organic polymer precursor, such as polyimide precursor,is coated on the hard substrate.

The flexible substrate is required to be with the excellent propertiesof surface topography, thermo stability, low thermal expansioncoefficient and reliability. Particularly, along with the popularity ofthe smart phone, the smart phone is of more and more function. Thescreen is the mainly interactive interface with user. The highresolution and large size panel are extremely important. And, therequirement for the flexible electronic device is higher and higher.

In the fabrication of the flexible electronic device, presently,inorganic powder is doped into an inorganic material precursor with apurpose to obtain a coefficient of thermal expansion (CTE) of 20 ppm/°C. (SID2010, Jia-Ming Liu and so on, Invited Paper: High PerformanceOrganic-Inorganic Hybrid Plastic Substrate for Flexible Display andElectronics), and to control and improve dimensional and thermalstability thereof. However, it is still different from the coefficientof thermal expansion of the rigid substrate, for example, thecoefficient of thermal expansion of glass is 3.39 ppm/° C. Therefore,when fabricating the flexible electronic device, interlaminar stresswill generates, leading to a warp in the substrate, and subsequentlyleading to stripping or cracking of membrane. Finally, various displaydefects will incur.

Meanwhile, permeability of the flexible substrate to oxygen or moistureis also important. For example, the organic light-emitting diode iseasily affected by the oxygen or the moisture because the permeation ofthe oxygen or the moisture reduces the function and life of the organiclight-emitting diode.

The de-bonding technology means a such technology where after a requiredelectronic device is fabricated from a flexible substrate attached to arigid substrate, such as glass, the flexible substrate and the rigidsubstrate are separated.

However, in the above de-bonding process, the amorphous silicon isapplied as sacrificial layer and laser equipment is applied.Consequently, the cost of the product is high.

FIG. 1 is a structure diagram for de-bonding layer disclosed by ITRI inrelated art. As shown in FIG. 1, ITRI disclosed a technology forde-bonding layer (SID2010, Cheng-Chung Lee and so on, Invited Paper: ANovel Approach to Make Flexible Active Matrix Displays): successively,Layer 12 is stuck on Rigid Glass Substrate 11, wherein, Layer 12 has asuitable bonding ability; next, a solution of PI precursor is coatedwith a coating area bigger that de-bonding layer area; next, the PIsolidifies to form PI Membrane 13; next, normal TFT process isactualized on PI Membrane 13 to form Device, such as TFT 14; finally, PIMembrane 13 is cut along with edges of DBL layer, Layer 12. The bondingability of PI Membrane 13 to Layer 12 is weak, consequently, Layer 12can be easily separated from the PI membrane after the cutting process.

The above-mentioned de-bonding technology is simplified. However. PIMembrane directly contacts to Rigid Substrate 11 at outer parts thereof,the generated cohesive force will lead to an inaccurate alignment in TFTprocess.

Furthermore, in the above-mentioned process, a gas barrier layer(containing SiN_(x) and composite layer) is formed on PI Membrane tosolve the problem of permeability. The gas barrier layer, in part,overcomes the permeability of water/oxygen of PI Membrane 13. However,there is still a difference of coefficient of thermal expansion, leadingto an inaccurate alignment in the following TFT process because ofstress. Particularly, when the technology is carried out on a biggersize glass substrate, bigger than that of G2 generation, the problemwill be more serious. Therefore, the yield rate of product is decreased.

U.S. Patent No. 2008309867A1 has disclosed a fabrication of a thin-filmflexible electronic device of the screen type that includes a pluralityof thin-film components on a glass support a starting support isprepared, including a rigid bulk substrate and a glass sheet fastened tothe rigid bulk substrate by reversible direct bonding so as to obtain aremovable interface. The plurality of thin-film components arefabricated on the glass sheet. The glass sheet is separated from therigid bulk substrate by disassembling the interface and, the glass sheetand the plurality of thin-film components are transferred to a finalsupport.

Korea Patent No. 20040111403A has disclosed an organic luminescencedevice and its production method. An organic luminescence device uses asubstrate with a gas-barrier film in which a gas-barrier film containingan amorphous oxide and at least two kinds of oxides selected from thegroup consisting of boron oxide, phosphorus oxide, sodium oxide,potassium oxide, lead oxide, titanium oxide, magnesium oxide, and bariumoxide is formed on a substrate. The selected two kinds of oxides are acombination of an oxide of an element having a large atomic radius andan oxide of an element having a small atomic radius. The substrate ismade of glass or plastic. As a result, the organic luminescence deviceusing a substrate excellent in gas-barrier capability to prevent theinfiltration of oxygen, water vapor and so on. from outside is provided.Consequently, it did not solve the problem of increasing the cost.

SUMMARY OF THE INVENTION

An embodiment of the present disclosure is directed toward a flexibleelectronic devices capable of effectively improve the dimensionalstability of plastic substrate and the water/oxygen barrier property offlexible substrate during the PI film fabrication and the follow-upprocess, improving the yield rate of good products and prolonging theworking life thereof.

A flexible electronic device, comprising:

(a) a substrate:

(b) a separating layer partly covering the substrate;

(c) an inorganic membrane, having a rough upper surface, covering sidewalls and an upper surface of the separating layer, and covering anexposed upper surface of the substrate;

(d) a display device substrate covering side walls and an upper surfaceof the inorganic membrane, and partly covering an exposed upper surfaceof the substrate;

(e) electronic components configured on surface of the display devicesubstrate.

Preferably, the inorganic membrane is a membrane formed by means ofPlasma Enhanced Chemical Vapor Deposition process.

Preferably, the inorganic membrane is a membrane which is quickly formedby means of Plasma Excitation Power, at a temperature lower than 200°C., with mixed gas including silane predominates.

Preferably, a thickness of the inorganic membrane is less than 300 nm.

Preferably, the material of the inorganic membrane is amorphous siliconor silicon nitride.

Preferably, adhesive force between the separating layer and thesubstrate is less than a preconfigured value.

Preferably, the separating layer is double side adhesive material.

Preferably, the roughness of the upper surface of the inorganic membraneis no less than Rz 0.2 μm and no more than Rz 0.3 μm.

Preferably, a material of the substrate is glass.

BRIEF DESCRIPTIONS OF THE DRAWINGS

The accompanying drawings, together with the specification, illustrateexemplary embodiments of the present disclosure, and, together with thedescription, serve to explain the principles of the present disclosure.

FIG. 1 shows structure diagram of the de-bonding layer technologydisclosed by ITRI in the related art;

FIGS. 2 to 4 show a flow diagram of the formation of the flexibleelectronic device of the present disclosure.

DESCRIPTIONS OF THE PREFERRED EMBODIMENTS

Hereinafter, certain exemplary embodiments according to the presentdisclosure will be described with reference to the accompanyingdrawings.

In this embodiment, first, a separating layer is formed on upper surfaceof a rigid substrate, such as glass, for example, a double sidedadhesive material is stuck to the glass substrate as the separatinglayer in the follow-up process, where the separating layer partly coversthe rigid substrate; next an inorganic membrane is deposited, forexample, the inorganic membrane is amorphous silicon or silicon nitridemembrane formed by means of Plasma Enhanced Chemical Vapor Depositionprocess, to cover the side walls and the upper surface of the separatinglayer, and the inorganic membrane also covers the exposed part of theupper surface of the rigid substrate; finally, a precursor of plasticsubstrate is coated to cover the side walls and the upper surface of theinorganic membrane, and partly cover the exposed part of the uppersurface of the rigid substrate; after solidification, the plasticsubstrate forms a display device substrate, and electronic componentsare set up on surface of the display device substrate.

Preferably, the roughness of the upper surface of the inorganic membraneis more that or equal to Rz 0.2 μm and less than or equal to Rz 0.3 μm.Meanwhile, preferably, the adhesive force between the separating layerand the rigid substrate is less than a preconfigured value. Thepreconfigured value can be adhesive force of separating layer to theinorganic membrane. Alternatively, the preconfigured value can be theadhesive force of inorganic membrane to substrate of the display device.

FIGS. 2 to 4 show a flow diagram of the formation of the flexibleelectronic device of the present disclosure. FIGS. 2 to 4 show that,first, Separating Layer 22 is formed on upper surface of Rigid Substrate21 to partly cover Rigid Substrate 21. Rigid Substrate 21 can be, forexample, glass substrate. Separating Layer 22 can be, for example,double sided adhesive material.

Next. Inorganic Membrane 23 is deposited to cover the side walls and theupper surface of Separating Layer 22. Inorganic Membrane 23 can beamorphous silicon, such as silicon hydride, or silicon nitride membraneformed by means of Plasma Enhanced Chemical Vapor Deposition process.Specifically, at the temperature lower than 200° C., such as 200° C.190° C., 180° C., 170° C. 150° C., 120° C. and so on, Inorganic Membrane23 is quickly formed on Separating Layer 21, by means of powder ofPlasma Excitation with mixture gas where silane predominates. InorganicMembrane 23 covers the side walls and the upper surface of SeparatingLayer 22, and also covers the exposed part of the upper surface of RigidSubstrate 21. In this embodiment, the thickness of Inorganic Membrane 23can be less than 300 nm, such as 100 nm, 150 nm, 200 nm, 300 nm, and soon.

Preferably, Upper Surface 231 of Inorganic Membrane 23 is a roughsurface, i.e., Upper Surface 231 has a roughness. Inorganic Membrane 23effectively improves the dimensional stability of plastic substrate andthe water/oxygen barrier property of flexible substrate during the PIfilm fabrication and the follow-up process, improving the yield rate ofgood products and prolonging the working life thereof, wherein, theroughness of Upper Surface 231 can be more that or equal Rz 0.2 μm andless that or equal to Rz 0.3 μm, such as Rz 0.2 μm, Rz 0.24 μm, Rz 0.26μm, Rz 0.28 μm or Rz 0.3 μm and so on. The roughness of Upper Surface231 is measured according to Ten Height Points of Microscopic Planeness.

Next, a precursor of plastic substrate, such as PI solution, is coatedto cover the side walls and Upper Surface 231 of the Inorganic Membrane23, and partly cover the exposed part of the upper surface of the RigidSubstrate 21; after solidification process, the plastic substrate formsDisplay Device Substrate 24.

Finally, Electronic Component 25, such as TFT, where ElectronicComponent 25 is not limited by TFT, is set up on surface of DisplayDevice Substrate 24. After fabricating Electronic Component 25, DisplayDevice Substrate 24 is cut along with inner edge of Separating Layer 22,for example, the position expressed by Arrow 26. The adhesive forcebetween Separating Layer 22 and Rigid Substrate 21 is not strong,therefore the fabricated electronic device, including remaining displaydevice substrate, remaining inorganic membrane and remaining separatinglayer, after cutting, can be easily de-bonded form Rigid Substrate 21,to complete the fabrication of a display device with a display substrateand an inorganic membrane.

In this embodiment, preferably, the adhesive force between SeparatingLayer 22 and Rigid Substrate 21 is less than a preconfigured value. Thepreconfigured value can be adhesive force of Separating Layer 22 toInorganic Membrane 23; or the preconfigured value can be adhesive forceof Inorganic Membrane 23 to Display Device Substrate 24, to ensure thefollow-up de-bonding process running smoothly, in the case that theadhesive force of Separating Layer 22 to Rigid Substrate 21 can meet therequirement of carrying out follow-up process, where after the cuttingprocess, a separating process of remaining separating layer form RigidSubstrate 21.

While the present disclosure has been described in connection withcertain exemplary embodiments, it is to be understood that the inventionis not limited to the disclosed embodiments, but, on the contrary, isintended to cover various modifications and equivalent arrangementsincluded within the spirit and scope of the appended claims, andequivalents thereof.

What is claimed is:
 1. A flexible electronic device, comprising: (a) asubstrate; (b) a separating layer partly covering the substrate; (c) aninorganic membrane, having a rough upper surface, covering side wallsand an upper surface of the separating layer, and covering an exposedupper surface of the substrate; (d) a display device substrate coveringside walls and an upper surface of the inorganic membrane, and partlycovering an exposed upper surface of the substrate; (e) electroniccomponents configured on surface of the display device substrate.
 2. Theflexible electronic device as disclosed in claim 1, wherein theinorganic membrane is a membrane formed by means of Plasma EnhancedChemical Vapor Deposition process.
 3. The flexible electronic device asdisclosed in claim 1, wherein the inorganic membrane is a membrane whichis quickly formed by means of Plasma Excitation Power, at a temperaturelower than 200° C., with mixed gas including silane predominates.
 4. Theflexible electronic device as disclosed in claim 1, wherein a thicknessof the inorganic membrane is less than 300 nm.
 5. The flexibleelectronic device as disclosed in claim 1, wherein the material of theinorganic membrane is amorphous silicon or silicon nitride.
 6. Theflexible electronic device as disclosed in claim 1, wherein adhesiveforce between the separating layer and the substrate is less than apreconfigured value.
 7. A flexible electronic device as disclosed inclaim 1, wherein the separating layer is double side adhesive material.8. The flexible electronic device as disclosed in claim 1, wherein theroughness of the upper surface of the inorganic membrane is no less thanRz 0.2 μm and no more than Rz 0.3 μm.
 9. The flexible electronic deviceas disclosed in claim 1, wherein a material of the substrate is glass.